| REGOL
450 TC WEAR PLATE Put Titanium Technology to Work for You |
|||
|
Field tests of two Cat 793 Haul Trucks lined at a Utah copper mine along side 4 competitors 500 BHN Wear Plates fount that after 24 months of service, or 12,725 hours the REGOL 450 TC trucks had worn approx. 1/8" at the worst point. This projects a 40,000 hour wear life on these trucks which is a 100% improvement over any other 500 Brinell wear plate previously tested at this mine. The same wear life improvement has been realized in haul trucks, chutes, and conveyor parts at several other mines. These field test results are a real testament to titanium technology. For additional test results, contact us. Independent lab tests support what field tests prove, REGOL 450 TC is the most cost effective and long lasting wear plate. A DSRW test done to ASTM G65 Procedure B (2000 revs.) 1/2" thick sample yields these results: |
|||
| Hardness | Weight
Loss (g) AFS 50-70 Sand |
Weight
Loss (g) Flattery Sand |
|
| Air
Hardening Steel 425 BHN AR Q & T REGOL 450 TC |
475
BHN 418 BHN 434 BHN |
0.587 0.653 0.444 |
0.167/0.167 0.159/0.161 0.123/0.120 |
Stock Sizes: 96" x 288" Average Plate Hardness: 450 BHN Titanium HV Hardness: 3200 Tests 1/2" Thick Material: 1/4"• 3/8"• 1/2"• 3/4"• 1"• 1-1/4 • 1-1/2"• 2"• 2-1/2" Yield: 181,000 Tensile: 211,000 Charpy Impacts @ 32 deg. = 18 ft./lbs. |
|||
|
Improved abrasion resistance is achieved from the carbide matrix and the martensite developed by a special heat treating process. Nickel, Moly., Boron and other alloying elements are also added to enhance abrasion resistant properties. |
|||||
Chemical Composition REGOL 450 TC |
|||||
| Carbon .29 |
Silicon .34 |
Manganese .69 |
Phosphate .007 |
Sulfur .001 |
Chromium .93 |
Mill Certifications with Shipment on Request |
|||||